strong base anion exchange resin

Anion exchange resin provide for optimum performance in deionization decolorization treatment for waste water

1.Carried standard :DL/T519-2004

2. Physical & chemical properties

Item

201×7 0H/Cl

201×7FC  OH/Cl

201×7 MB OH/Cl

201×7 SC OH/Cl

water content      (%)

53.00-58.00/42.00-48.00

Regenerative capacity of the largest mmol/g ≥

3.80/-

Strong base mission capacitymmol/g ≥

3.60/3.50

Volume exchange capacity(mmol/ml) ≥

1.10/1.35

1.05/1.30

Apparent density(wet)     (g/ml)

0.66-0.71/0.67-0.73

Ture density(wet)     (g/ml)

1.060-1.090/1.070-1.100

Size        (%)

(0.315 -1.250mm ) ≥95.0

(0.450 -1.250mm ) ≥95.0

(0.400 -0.900mm ) ≥95.0

(0.630 -1.250mm )≥95.0

(< 0.315mm ) ≤1.0

(< 0.450mm ) ≤1.0

-

(< 0.630mm ) ≤1.0

Effective grain diameter      mm

0.400-0.700

≥0.500

0.500-0.800

≥0.630

coefficient of uniformity       ≤

1.60

1.40

Globle ratio    (%)  ≥

60.00

Appearance

Browm yellow browm beack

Form

Cl

Application

Currency-bed system

Flotating-bed system

Mixed-bed system

double-deck bed

Fuctional groups

-N+(CH3)3

-N+(CH3)3

-N+(CH3)3

-N+(CH3)3

appearance : slight yellow color transparent spherical articles.

1.   Lonic form as delivered :Cl- form

Reference working data:

1.  PH value range:0----14

2.  Working temperature : Cl form <80 , OH form <60

3.  Swelling :%(Cl----OH-)

4.  Height  of  resin layer for industrical use : m 1.0---3.0

5.  Concentration of regenerant solution :%: NaOH:4---5

6.  Amount of used regerant solution : kg/m3

Calculated in 100% NaOH(industrical) :40----80

7.  regenerant flow rata : m/h 4---6

8.  Regenerant  contact of time (minute): 30---60

9.  Rinse flow rate : m/h :15---25

10. Rinse time minute : approx  25

11. Service flow rate m/h:15---25

12. Operational capacity mmol /l (wet)>450

Application :

    The product is mainly  used in pure water and extremely pure wate preparation, also can be used in waste water treatment and preparation of biological product .

Package:

     Carton bucket with inner plastic bag

Net weight :25kgs

strong base anion exchange resin